Estimation of dislocation concentration in plastically deformed FeCrNi alloy by positron annihilation lifetime

摘要:Dislocations would be induced after plastic deformation, which might change the mechanical properties of solids. FeCrNi austenitic model alloy and its Mo-diluted alloy were cold rolled with different degree of thickness reduction. Positrons are sensitive to point defects, which are easily trapped and annihilated around the trapping sites. The mean positron lifetimes have been used to estimate the average dislocation concentration in solids. Meanwhile, the trapping efficiency μ was calculated from the lifetime results. The trapping efficiency value is estimated about 3.31×10-7 cm3s-1 for FeCrNi alloy and 3.31×10-7 cm3s-1 for Mo-diluted alloy, respectively. The increment of the hardness value during plastic deformation is related to the increase of the dislocation density and dislocation pile up in solids.

版本历史

[V1] 2017-03-26 19:36:59 chinaXiv:201703.00586V1 下载全文
点击下载全文
同行评议状态
待评议
许可声明
metrics指标
  • 点击量2808
  • 下载量1649
评论
分享
邀请专家评阅