Study on the corrosion behavior of 316H stainless steel in molten NaCl-KCl-MgCl2 salts with and without purification

请选择邀稿期刊:
摘要: The corrosion behavior of 316H stainless steel (SS) in the impure and purified NaCl-KCl-MgCl2 salt was investigated at 700 °C . Results indicate that the main deleterious impurity induced corrosion in the impure salt was the absorbed moisture, present in the form of MgCl2·6H2O. 316H SS occurred severe intergranular corrosion with a corrosion depth of 130 μm for 1000 h in the impure NaCl-KCl-MgCl2 salt. In contrast, the purification treatment of molten chloride salt by the dissolved Mg metal can remove the absorbed moisture, and the corresponding reactions were also discussed. As a result, the corrosiveness of NaCl-KCl-MgCl2 salt is reduced significantly. 316H SS occurred slight uniform corrosion with a depth of less than 5 μm for 3000 h in the purified NaCl-KCl-MgCl2 salt.


 

版本历史

[V1] 2023-11-16 16:59:42 ChinaXiv:202311.00205V1 下载全文
点击下载全文
预览
同行评议状态
通过
许可声明
metrics指标
  •  点击量207
  •  下载量22
评论
分享