A study of Cu precipitates in Fe ions irradiated Fe-Cu alloys by positron annihilation techniques

分类： 物理学 >> 凝聚态:结构、力学和热性能 提交时间： 2017-03-26

X. Z. Cao P. Zhang Q. Xu G. D. Cheng H. B. Wu X. P. Jiang R. S. Yu L. Wei B. Y. Wang

摘要： Cu precipitates played a key factor in irradiation induced hardening and embrittlement of reactor pressure vessel (RPV).In this work, two kinds of Fe-Cu model alloys with different Cu contents irradiated by Fe ion at 573 K were investigated using positron annihilation techniques and SEM. Doppler Broadening Spectroscopy(DBS) results indicated that with the irradiation dose increased from 0.1 dpa to 1.2 dpa, more vacancy-type defects were induced during Fe ion irradiation, and with different Cu contents, defects condition had few changes. Coincident Doppler Broadening (CDB) results indicated Cu precipitates were formed during the irradiation, which could be verified through the SEM results. The CDB results also showed that the Cu precipitates were the same at 0.1 dpa between the samples with different Cu contents. In Fe0.6Cu samples, more Cu precipitates were formed than that of Fe0.3Cu sample at 1.2 dpa.

同行评议状态:待评议

 点击量 1781  下载量 975  评论